High speed steel

High speed steel (HSS) – round and flat from stock

Chipping tools for this process must adapt to the material we want to chip. High speed steels are mainly used for chipping.

At these materials cutting power and cutting performance survive up to a temperature of 600° C. Because of modern machinery and of an optimized machining process high speed steel standards are always most important.

Due to special processes during the steel melting casting and processing a high quality level can be guaranteed. To achieve the best characteristics of the material and a long durability it is most important to have the best adjustment of the elements. By different usage of carbon, chrome, molybdenum, vanadium, tungsten and cobalt the favored characteristics of the high speed steels can be achieved. You will find the most common high speed grades in our delivery program.

The information in the following table according to GOST grades are for your information only, without liability.

Stock Program

Data Sheet DIN EN ISO 4957 Product Form
1.3243 HS6-5-2-5
EN ISO 4957:
HS6-5-2-5
AFNOR:
Z85WDKCV06-05-02 Z85WDKCV06-05-05-04-02
BS:
BM 35
UNE:
F.550.C (F.5613)
AISI / SAE:
M 35
GOST:
?6 ?5 ?5 S6
C%:
0,92
Mn%
< 0,40
Si%:
< 0,45
Cr%:
4,10
S%:
-
P%:
-
Heat treatment
- annealing
800 - 860
- hardening
1190 - 1230
- tempering
acc. tempering chart
1.3247 HS2-9-1-8
EN ISO 4957:
HS2-9-1-8
AFNOR:
Z110DKWCV09-08-04-02-01
BS:
BM 42
UNE:
F.5617
AISI / SAE:
M 42
GOST:
?2 ?10 ?8
C%:
1,10
Mn%
< 0,40
Si%:
< 0,70
Cr%:
4,00
S%:
-
P%:
-
Heat treatment
- annealing
800 - 860
- hardening
1160 - 1190
- tempering
acc. tempering chart
1.3343 HS6-5-2C
EN ISO 4957:
HS6-5-2C
AFNOR:
Z85WDCV06-05-04-02
BS:
BM 2
UNE:
F.550.A (F.5604)
AISI / SAE:
M 2
GOST:
?6 ?5
C%:
0,90
Mn%
< 0,40
Si%:
< 0,45
Cr%:
4,10
S%:
-
P%:
-
Heat treatment
- annealing
770 - 860
- hardening
1190 - 1230
- tempering
acc. tempering chart
1.3346 -
EN ISO 4957:
-
AFNOR:
Z85DCVW08-04-02-01
BS:
~ BM1
UNE:
-
AISI / SAE:
M 1
GOST:
-
C%:
0,82
Mn%
< 0,40
Si%:
< 0,45
Cr%:
3,80
S%:
-
P%:
-
Heat treatment
- annealing
770 - 840
- hardening
1170 - 1210
- tempering
acc. tempering chart
1.3390 -
EN ISO 4957:
-
AFNOR:
-
BS:
-
UNE:
-
AISI / SAE:
-
GOST:
-
C%:
0,88
Mn%
-
Si%:
-
Cr%:
4,00
S%:
-
P%:
-
Heat treatment
- annealing
770 - 840
- hardening
1170 - 1210
- tempering
1.3392 -
EN ISO 4957:
-
AFNOR:
-
BS:
-
UNE:
-
AISI / SAE:
M 52
GOST:
-
C%:
0,85
Mn%
0,35
Si%:
0,35
Cr%:
4,20
S%:
-
P%:
-
Heat treatment
- annealing
770 - 840
- hardening
- tempering

Calculator